What is caustic cracking or embrittlement? What is its cause? Suggest remedy This is

This is a form of intercrystalline/intergrannular cracking and occurs when a specific corrodent  and sufficient tensile stress exists. Iron consists of ferritic granules bonded by iron carbide so  this gives a scope of the intergrannular corrosion. This can be found in water tubes, super  heater, reheat tubes, and in stressed components of the water drum. The stress may be due  to thermal, bending or residual stress (due to welding). This usually occurs as a localized  attack in the combination of NaOH, some soluble silica and a tensile stress. The mechanism  begins with the accumulation of the corrodent NaOH due to – 
a. DNB (departure from nucleate boiling) 
b. Deposition 
c. Evaporation at the water line 
d. Small leakage 
e. High heat flux (rapid evaporation) 
f. High pressure

This corrosion below 149˚C or with NaOH concentration below 5% is rare. Increased 
susceptibility occurs at about 20~40%. This corrosion is difficult to identify in the beginning 
and ND testing has to be carried out at the suspected areas. At some time after the initial 
start of the corrosion, this manifests as a whitish highly alkaline deposits or sparkling 
magnetite. 

COUNTER MEASURES: 
a. Applying heat treatment process to relieve stresses after fabrication/repairs (welding 
etc) 
b. Correct and accurate boiler water treatment 
c. Avoid DNB 
d. Avoid accumulation of the deposits 
e. Prevent leakage of corrodents 
f. Prevent carryover 
g. Use of rifling in the water tubes

Comments

Post a Comment

If you have any doubts.Please let me know

Popular posts from this blog

Differences between MC/MC-C and ME/ME-C engines

The electrohydraulic control mechanisms of the ME engine replace the following components of the conventional MC engine: Chain drive for camshaft Camshaft with fuel cams, exhaust cams and indicator cams Fuel pump actuating gear, including roller guides and reversing mechanism Conventional fuel pressure booster and VIT system Exhaust valve actuating gear and roller guides Engine driven starting air distributor Electronic governor with actuator Regulating shaft Engine side control console Mechanical cylinder lubricators. The Engine Control System of the ME engine comprises: Control units Hydraulic power supply unit Hydraulic cylinder units, including: Electronically controlled fuel injection, and Electronically controlled exhaust valve activation Electronically controlled starting air valves Electronically controlled auxiliary blowers Integrated electronic governor functions Tacho system Electronically controlled Alpha lubricators
9 comments
Read more

Main engine interlocks

Interlocks are provided so that the engine can be started or reversed only when certain conditions have been fulfilled. When there is a remote control of engines, it is essential to have interlocks. This reduces the possibility of engine damage and any hazards to the operating personnel. Turning gear Interlock . This device prevents the engine from being started if the Turning gear is engaged. Running Direction Interlock . This prevents the fuel from being supplied if the running direction of the engine does not match the Telegraph. Starting Air Distributor in end position . This prevents starting from taking place if the shifting of the Distributor has not been completed. Main Lube. oil pressure, Piston cooling pressure, Jacket water pressure, and important parameters must be above the required minimum. Auxiliary Blower Interlock . The Auxiliary Blower is provided in case of Constant pressure turbo charging. Air Spring pressure Interlock . In case of the present generation
7 comments
Read more

Why is a man hole door elliptical in shape?

Any opening in a pressure vessel is kept to a minimum and for a man entry an elliptical hole  is lesser in size than the corresponding circular hole. More over it is prime concern to have a  smoothed generous radius at the corners to eliminate stress concentration. Hence other  geometrical shapes like rectangle and square are ruled out.  To compensate for the loss of material in the shell due to opening, a doubler ring has to be  provided around the opening. The thickness of the ring depends on the axis length along the  dirrection in which the stresses are maximum and the thickness of the shell. It is important to  align the minor axis along the length of the vessel, as the stress in this direction is  maximum. Longitudinal stress: Pd/2t where P= pressure inside the vessel, d= diameter of the arc, t=  thickness of the shell plating  Circumferential stress: Pd/4t  More over a considerable material and weight saving is achieved as minor is along the  direction of maximum stress.
20 comments
Read more